 Post subject: Seperating Natural from Heated Citrine
PostPosted: Thu Feb 14, 2019 3:10 pm 
Offline
Site Admin
User avatar

Joined: Sun Oct 16, 2005 12:22 pm
Posts: 21602
Location: San Francisco
When I was in Tucson at the AGA meeting, I spoke with Dr. Claudio Milisenda who has been with the German Gemmological Association (DGemG) and it considered an expert on quartz.

Naturally occurring citrine is dichroic.
Heated amethyst is not.


Top
 Profile  
Reply with quote  
 Post subject: Re: Seperating Natural from Heated Citrine
PostPosted: Thu Feb 14, 2019 6:05 pm 
Offline
Gold Member

Joined: Wed Jan 23, 2013 5:29 pm
Posts: 1047
Location: Paris
I think it was on this forum that somebody once gave the reference of this excellent article from 2013 about the colors of quartz. I have printed it and sometimes re-read it with delight, it is so very clear.

http://ctminsoc.org.za/articles/the-colours-of-quartz

If a citrine is natural, it is Al-bearing, and it is pleochroic.
If it is issued from a Fe-bearing amethyst heat treated, it will not show pleochroism.


Top
 Profile  
Reply with quote  
 Post subject: Re: Seperating Natural from Heated Citrine
PostPosted: Thu Feb 14, 2019 11:14 pm 
Offline
Moderator
User avatar

Joined: Mon Apr 02, 2012 9:31 pm
Posts: 4015
Location: North Carolina
I like the phrasing on that, Isi, though I am willing to believe there could be natural occurrences of 'heated amethyst' type citrine somewhere (not that it would ever be easy to prove it!). Of course pleochroism likely won't help with radiation-induced colors since those are also li/al based.

_________________
Rough and cut classic and exotic synthetic gems:https://store.turtleshoard.com


Top
 Profile  
Reply with quote  
 Post subject: Re: Seperating Natural from Heated Citrine
PostPosted: Fri Feb 15, 2019 12:26 pm 
Offline
Site Admin
User avatar

Joined: Sun Oct 16, 2005 12:22 pm
Posts: 21602
Location: San Francisco
Perhaps there may be naturally occurring heated amethyst....do we need to concern ourselves with it?

If one wishes to buy or sell unheated citrine i would suggest sticking to material which can be separated with pleochroism.

The other possibilities (or probabilities) are subjects for mineralogical doctoral projects...or post doctoral projects, (Right up the Challener's street by the way), but perhaps not something the average citrine buying gemologist should be too concerned about.

Thoughts?


Top
 Profile  
Reply with quote  
 Post subject: Re: Seperating Natural from Heated Citrine
PostPosted: Fri Feb 15, 2019 6:37 pm 
Offline
Moderator
User avatar

Joined: Mon Apr 02, 2012 9:31 pm
Posts: 4015
Location: North Carolina
I'd say if you want untreated citrine you need to buy uncut rough close to the source and have it cut yourself. Zambian rough can be bought this way easily, with a crystal form that is sufficiently distinctive to exclude it being typical amethyst starting material for heating.
I don't think irradiated citrine is very obscure though. Aside from lemon quartz which is irradiated, pleochroic and ubiquitous there are other less obvious hues that can be produced that way, many of which the late Liccini mentioned on his webpage. So I would not take pleochroism alone as an effective defense against treatment, just for separating 'heated amethyst' style citrine from al/li citrine or however you prefer to call it.
Aside from that, in my opinion the broadest and most interesting color range of citrines are treated one way or the other, so if you like citrine you should just accept that.

_________________
Rough and cut classic and exotic synthetic gems:https://store.turtleshoard.com


Top
 Profile  
Reply with quote  
 Post subject: Re: Seperating Natural from Heated Citrine
PostPosted: Fri Feb 15, 2019 7:50 pm 
Offline
Site Admin
User avatar

Joined: Sun Oct 16, 2005 12:22 pm
Posts: 21602
Location: San Francisco
Stephen wrote:
in my opinion the broadest and most interesting color range of citrines are treated one way or the other, so if you like citrine you should just accept that.


I agree, but over the years we routinely get queries on identifying unheated citrine, so I thought it would be a good idea to post my new information. :D


Top
 Profile  
Reply with quote  
 Post subject: Re: Seperating Natural from Heated Citrine
PostPosted: Wed May 29, 2019 12:42 am 
Offline
Valued Contributor

Joined: Tue Nov 04, 2008 11:59 pm
Posts: 160
Location: Hong Kong
I wonder what happens when Ameythst is re-heated? Does it revert back to Citrine color?

_________________
Sera
www.zahaetcetera.com


Top
 Profile  
Reply with quote  
 Post subject: Re: Seperating Natural from Heated Citrine
PostPosted: Thu May 30, 2019 3:21 pm 
Offline
Gold Member

Joined: Wed Jan 23, 2013 5:29 pm
Posts: 1047
Location: Paris
It's the other way round...
If a citrine is re-heated, does it come back to amethyst ?
In my experience, no ; next step is : it turns milky, and then, it cracks.


Top
 Profile  
Reply with quote  
Display posts from previous:  Sort by  
Post new topic Reply to topic  [ 8 posts ] 

All times are UTC - 4 hours


Who is online

Users browsing this forum: No registered users and 5 guests


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Search for:
Jump to:  
Powered by phpBB © 2000, 2002, 2005, 2007 phpBB Group
Gemology Style ported to phpBB3 by Christian Bullock